A-PI-260S Polyimide
A-PI-260S is a thermoplastic polyimide resin with an amber appearance. It has the advantages of high temperature resistance, high strength, wear resistance, self-lubrication, chemical resistance, and radiation resistance.
Product Applications
Used to manufacture high-temperature resistant precision parts, insulating parts, wear-resistant parts, seals and other parts; The products are widely used in aerospace, semiconductor industry, petroleum industry and other fields.
Aerospace
Semiconductor Industry
Petroleum Industry
Performance Data
Mechanical properties tested at 23°C and 220°C, including hardness, strength, density, and wear resistance using standard methods.
|
Test Features |
Test Method |
Unit |
Test Conditions |
Results |
|---|---|---|---|---|
|
Bulk density |
GB/T 16913-2008 |
g/cm³ |
23°C |
0.35 |
|
Particle size (D50) |
GB/T 19077-2016 |
µm |
23°C |
10 |
|
Rockwell hardness |
GB/T 3398.2-2008 |
HRE |
23°C |
63 |
|
Molding density |
GB/T 4472-2011 |
g/cm³ |
23°C |
1.36 |
|
Impact strength |
GB/T 1043.1-2008 |
kJ/m² |
23°C |
230 |
|
Flexural Strength |
GB/T 9341-2008 |
MPa |
23°C 220°C |
163 62 |
|
Flexural modulus |
GB/T 9341-2018 |
MPa |
23°C 220°C |
3400 1600 |
|
Tensile Strength |
GB/T 1040.1-2008 |
MPa |
23°C 220°C |
125 65 |
|
Elongation |
GB/T 1040.1-2018 |
% |
23°C 220°C |
28 56.7 |
|
Compressive strength |
GB/T 1041-2008 |
MPa |
1% Deformation |
468 |
|
Compressive modulus |
GB/T 1041-2008 |
MPa |
23°C |
3930 |
|
Linear thermal expansion coeff. |
ASTM D696-16 |
/°C |
296~537K |
47.885x10⁻⁶ |
|
Volume resistivity |
GB/T 31838.2-2019 |
Ω·cm |
23°C |
4.336x10¹² |
The above data are product sample measurement values, not guaranteed values; All products are formed by compression, with a certain degree of directionality.