A-PI-5001 Polyimide
A-PI-5001 is a high-rigidity polyimide resin. Compared with other polyimide products, it has higher modulus, higher hardness, and better dimensional stability under high temperature conditions.
Product Applications
Used to manufacture high temperature resistant seals, wear resistant parts, transmission parts, insulation parts, chip test fixtures and other precision parts. Mainly used in aerospace, semiconductor industry, automobile industry, petroleum industry, special industry and other fields.
Aerospace
Semiconductor Industry
Automotive Industry
Petroleum Industry
Special Industry
Contact Us
Performance Data
Mechanical properties tested at 23°C and 300°C, including hardness, strength, density, and wear resistance using standard methods.
|
Test Features |
Test Method |
Unit |
Test Conditions |
Results |
|---|---|---|---|---|
|
Rockwell Hardness |
GB/T 3398.2-2008 |
HRE |
23°C |
92 |
|
Impact strength of unnotched simply supported beams |
GB/T 1043.1-2008 |
kJ/m² |
23°C |
98 |
|
Flexural Strength |
GB/T 9341-2008 |
MPa |
23°C 300°C |
237 78 |
|
Flexural Modulus |
GB/T 9341-2008 |
MPa |
23°C 300°C |
5119 2417 |
|
Tensile Strength |
GB/T 1040.1-2018 |
MPa |
23°C 300°C |
135 53 |
|
Elongation at break |
GB/T 1040.1-2018 |
% |
23°C 300°C |
7.2 37.1 |
|
Compressive Strength |
GB/T 1041-2008 |
MPa |
1% Deformation 10% Deformation |
22 118 |
|
Poisson's ratio |
ASTM D638-10 |
/ |
23°C |
/ |
|
Surface Resistance |
IEC 61340 |
Ω |
23°C |
10¹⁴-10¹⁵ |
|
Density |
GB/T 1033.1-2008 |
g/cm³ |
23°C |
1.43 |
|
Friction coefficient |
GB/T 3960-2016 |
/ |
2h |
0.15 |
|
Mass of wear |
GB/T 3960-2016 |
mg |
2h |
4 |
|
Absorption |
GB/T 1034-2008 |
% |
24h 48h |
0.11 0.18 |
The above data are product sample measurement values, not guaranteed values; All products are formed by compression, with a certain degree of directionality.