A-PI-L8 Polyimide
A-PI-L8 is a cold pressed polyimide resin, which has advantages such as high and low temperature resistance, high insulation, high mechanical strength, and good machining performance.
Contact Us
Product Applications
Used for manufacturing brake sensors, automotive glass lifting limit nails, eddy current rings, wear-resistant parts, insulation parts, high-temperature resistant components, etc. The product is widely used in the automotive industry, plasma cutting and other fields.
Automotive Industry
Plasma Cutting
Other Fields
Contact Us
Performance Data
Mechanical properties tested at 23°C and 260°C, including hardness, strength, density, and wear resistance using standard methods.
|
Test Features |
Test Method |
Unit |
Test Conditions |
Results |
|---|---|---|---|---|
|
Rockwell Hardness |
GB/T 3398.2-2008 |
HRE |
23°C |
12 |
|
Impact strength of unnotched simply supported beams |
GB/T 1043.1-2008 |
kJ/m² |
23°C |
30 |
|
Flexural Strength |
GB/T 9341-2008 |
MPa |
23°C 260°C |
80 42 |
|
Flexural Modulus |
GB/T 9341-2008 |
MPa |
23°C 260°C |
2216 1561 |
|
Tensile Strength |
GB/T 1040.1-2018 |
MPa |
23°C 260°C |
50 32 |
|
Elongation at break |
GB/T 1040.1-2018 |
% |
23°C 260°C |
5.3 4.2 |
|
Compressive Strength |
GB/T 1041-2008 |
MPa |
1% Deformation 10% Deformation |
22 104 |
|
Surface Resistance |
IEC 61340 |
Ω |
23°C |
>10¹² |
|
Density |
GB/T 4472-2011 |
g/cm³ |
23°C |
1.27 |
|
Friction coefficient |
GB/T 3960-2016 |
/ |
2h |
0.24 |
|
Mass of wear |
GB/T 3960-2016 |
mg |
2h |
9.8 |
|
Absorption |
GB/T 1034-2008 |
% |
24h 48h |
0.5 0.85 |
The above data are product sample measurement values, not guaranteed values; All products are formed by compression, with a certain degree of directionality.