A-PI-330 Polyimide
A-PI-330 is a high-performance polyi- mide resin, the product has advantages such as high temperature resistance, high insulation, selflubricating, low friction coefficient, low dielectric constant, chemical resistance, radiation resistance, heat deformation resistance, high mechanical strength, and good machining performance.
Product Applications
Used for manufacturing components such as high and low temperature resistant parts, wear resistant parts, insulation parts, oil-free bearings, valve seats, seals, chip test bases, etc. The product is widely used in aerospace, semiconducto industry,automotive industry, hot runner and other fields.
Aerospace
Semiconductor Industry
Automotive Industry
Hot Runner
Get Free Quote!
Performance Data
Mechanical properties tested at 23°C and 260°C, including hardness, strength, density, and wear resistance using standard methods.
|
Test Features |
Test Method |
Unit |
Test Conditions |
Results |
Competitor 1 |
Competitor 2 |
|---|---|---|---|---|---|---|
|
Rockwell Hardness |
GB/T 3398.2-2008 |
HRE |
23°C |
49 |
45 |
46 |
|
Impact strength of unnotched simply supported beams |
GB/T 1043.1-2008 |
kJ/m² |
23°C |
160 |
73 |
49 |
|
Flexural Strength |
GB/T 9341-2008 |
MPa |
23°C 260°C |
132 64 |
110 62 |
113 59 |
|
Flexural Modulus |
GB/T 9341-2008 |
MPa |
23°C 260°C |
3180 1754 |
3100 1724 |
3040 1667 |
|
Tensile Strength |
GB/T 1040.1-2018 |
MPa |
23°C 260°C |
107 41 |
86 41 |
88 41 |
|
Elongation at break |
GB/T 1040.1-2018 |
% |
23°C 260°C |
12.6 26.2 |
7.5 7 |
8 6 |
|
Compressive Strength |
GB/T 1041-2008 |
MPa |
1% Deformation 10% Deformation |
21 146 |
24 133 |
24 128 |
|
Coefficient of thermal expansion |
ASTM D-696 |
µm/m/k |
296~573K |
55 |
54 |
55 |
|
Shear Strength |
HG/T 3839-2006 |
MPa |
23°C |
101 |
89 |
/ |
|
Poisson's ratio |
ASTM D638-10 |
/ |
23°C |
0.36 |
0.41 |
0.37 |
|
Surface Resistance |
IEC 61340 |
Ω |
23°C |
>10¹² |
>10¹² |
>10¹² |
|
Density |
GB/T 4472-2011 |
g/cm³ |
23°C |
1.41 |
1.43 |
1.38 |
|
Friction coefficient |
GB/T 3960-2016 |
/ |
2h |
0.24 |
0.29 |
0.32 |
|
Mass of wear |
GB/T 3960-2016 |
mg |
2h |
4.4 |
7.6 |
/ |
|
Absorption |
GB/T 1034-2008 |
% |
24h 48h |
0.12 0.22 |
0.23 0.32 |
0.21 0.5 |
The above data are product sample measurement values, not guaranteed values; All products are formed by compression, with a certain degree of directionality.