A-PI-5050 Modified polyimide resin
A-PI-5050 is a modified polyimide resin with advantages such as high heat resistance, good thermal conductivity, excellent friction performance, and good machining performance.
Contact Us
Product Applications
Used for manufacturing hot glass grippers, sandwiches, paddles, push rods, bottle holders, pneumatic blades, etc. The product is widely used in the hot glass industry, general industry, and other fields.
Hot Glass Industry
General Industry
Other Fields
Performance Data
Key mechanical and physical properties are shown for both thermoforming and cold forming, with competitor comparison where available.
|
Test Features |
Test Method |
Unit |
Test Conditions |
Results (Thermoforming) |
Results (Cold forming) |
Competitor1 (Thermoforming) |
|---|---|---|---|---|---|---|
|
Rockwell Hardness |
GB/T 3398.2-2008 |
HRE |
23°C |
15 |
82(HRL) |
15 |
|
Impact strength of unnotched simply supported beams |
GB/T 1043.1-2008 |
kJ/m² |
23°C |
21 |
15 |
/ |
|
Flexural Strength |
GB/T 9341-2008 |
MPa |
23°C 260°C |
90 50 |
78 44 |
89.6 44.8 |
|
Flexural Modulus |
GB/T 9341-2008 |
MPa |
23°C 260°C |
7598 4695 |
5090 3164 |
4826 2758 |
|
Tensile Strength |
GB/T 1040.1-2018 |
MPa |
23°C 260°C |
68 31 |
46 26 |
52 23 |
|
Elongation at break |
GB/T 1040.1-2018 |
% |
23°C 260°C |
3.9 2.7 |
2.9 3.2 |
3 2 |
|
Compressive Strength |
GB/T 1041-2008 |
MPa |
1% Deformation 10% Deformation |
19 146 |
26 110 |
31 112 |
|
Shear Strength |
HG/T 3839-2006 |
MPa |
23°C |
46 |
/ |
/ |
|
Poisson's ratio |
ASTM D638-10 |
/ |
23°C |
0.24 |
/ |
/ |
|
Density |
GB/T 4472-2011 |
g/cm³ |
23°C |
1.72 |
1.62 |
/ |
|
Friction coefficient |
GB/T 3960-2016 |
/ |
2h |
0.15 |
0.16 |
0.3 |
|
Mass of wear |
GB/T 3960-2016 |
mg |
2h |
1.2 |
9.2 |
/ |
|
Absorption |
GB/T 1034-2008 |
% |
24h 48h |
0.04 0.08 |
0.6 0.81 |
0.14 0.42 |
The above data are product sample measurement values, not guaranteed values; All products are formed by compression, with a certain degree of directionality.